Irin alagbara Irin Yika Bar fun titẹ machining tabi Ige

Irin Alagbara Irin Yika Pẹpẹ fun titẹ machining tabi Ige ifihan aworan

Apejuwe kukuru:

Hebei Gangxin Technology Co., Ltd jẹ asiwaju Alagbara Irin Yika Bar išoogun ni China.Irin Alagbara Irin Yika Pẹpẹ jẹ ite irin alagbara irin austenitic alakikanju ti o lo ni ọpọlọpọ awọn ohun elo.A jẹ Olupese Pẹpẹ Yika Irin Alagbara ti a mọ daradara, Olupese, Onisowo, Oluṣowo, ati Olutaja ni Ilu China.Irin alagbara Irin Yika Ifi wa ni orisirisi awọn titobi lati pade EN, DIN, JIS, ASTM, BS, ASME, ati AISI awọn ibeere.Ni awọn ile-iṣẹ iṣelọpọ wa, a ṣe gbogbo awọn ọja Iyika Irin Alagbara Irin nipasẹ lilo imọ-ẹrọ tuntun.

Fi imeeli ranṣẹ si wa

Alaye ọja

ọja Tags

awọn ọja apejuwe

Irin Alagbara Irin Yika Ifi wa ni orisirisi kan ti onipò ti o ti wa ni lilo ni orisirisi awọn ile ise.Irin alagbara, irin yika ifi ti wa ni lilo nitori ti won agbara ati resistance si ipata.Chromium wa ninu gbogbo irin alagbara.Awọn ọpa Yika Irin alagbara, irin wa ni awọn iwọn ila opin ti o wa lati 4mm si 500mm.Awọn ipari ti awọn ọpa jẹ lati 1 si 6 mita.Awọn titobi aṣa ati gigun tun wa.A tun jẹ awọn olutaja ti Awọn ọpa Iyika 304 Yika Iyika, Irin Alagbara 304L Round Bars, Irin alagbara 316 Round Bars, ati bẹbẹ lọ.

Awọn pato Pẹpẹ Yika SS, Awọn iwọn, Awọn onigi:

Irin Alagbara, Irin Pẹpẹ Ipari	2 si 6 mita tabi 8 si 20 ẹsẹ
Irin alagbara, irin Rod Chamfering	Wa ni awọn iwọn 30, 45 & 60 nipasẹ ẹrọ mimu-ipari mejeeji ni kikun laifọwọyi
Ultrasonic igbeyewo of ASTM A276 Asapo Rod	Gẹgẹbi ASTM A-388, EN 10308 (kilasi 1 si 4), API 6A/ISO jẹ idanwo 100% nipasẹ Digital Ultrasonic Detector, 10423: 2003-PSL 3, MIL-STD 2154, SEP 1920: 1984
Irin Alagbara, Irin Yika Bar Iwon Tolerances	h11
Ifarada ti Cold Rolled SS Yika Pẹpẹ Ipari	Iṣura ni gige pataki si igi gigun ni ifarada - 0/+ 10mm (-0 +0.5 inch)
Dada Ipari ti Tutu yiyi SS Yika Bar	Tutu fa tabi Igbanu didan majemu
Yika Bar Heat Itoju	Annealed ati Solusan Annealed

SS Yika Pẹpẹ Mechanical Properties:

Ipele	Ilọsiwaju	iwuwo	Agbara fifẹ	Agbara ikore (0.2% aiṣedeede)	Ojuami Iyo
SS 202	40%	8.0 g / cm3	515 MPa	275 MPa	1454°C (2650°F)
SS 303	50%	55%	Psi - 85,000	Psi - 45,000	Rb 180
SS 304	40%	8.0 g / cm3	Psi – 75000, MPa – 515	Psi – 30000, MPa – 205	1400°C (2550°F)
SS 304L	40%	8.0 g / cm3	Psi – 75000, MPa – 515	Psi – 30000, MPa – 205	1400°C (2550°F)
SS 316	35%	8.0 g / cm3	Psi – 75000, MPa – 515	Psi – 30000, MPa – 205	1454°C (2650°F)
SS 316L	40%	8.0 g / cm3	485 min	170 min.	1400°C (2550°F)

SS Yika Pẹpẹ Kemikali:

Iwọn ASTM	Erogba	Manganese	Silikoni	Efin	phosphorous	Chromium	Nickel	Molybdenum	Omiiran
304	ti o pọju 0.08	2.00 ti o pọju	ti o pọju 0.75	ti o pọju 0.030	ti o pọju 0.045	18.0-20.0	8.0 11.0	–	–
316	ti o pọju 0.08	2.00 ti o pọju	ti o pọju 0.75	ti o pọju 0.030	ti o pọju 0.045	16.0-18.0	10.0 14.0	2.0 3.0	–
317L	ti o pọju 0.035	2.00 ti o pọju	ti o pọju 0.75	ti o pọju 0.030	ti o pọju 0.045	18.0-20.0	11.0 14.0	3.0 4.0	–
310 S	ti o pọju 0.08	2.00 ti o pọju	1.5 ti o pọju	ti o pọju 0.030	ti o pọju 0.045	24.0-26.0	19.0 22.0	3.0 4.0	–
347 H	0.04 0.10	2.00 ti o pọju	ti o pọju 0.75	ti o pọju 0.030	ti o pọju 0.045	17.0-19.0	9.0 13.0	–	10C(Cb+Ta) <1.10%
321	0.08	2.00 ti o pọju	ti o pọju 0.75	ti o pọju 0.030	ti o pọju 0.045	17.0-20.0	9.0 12.0	–	5C 0.70%

Apẹrẹ Iwọn Iwọn Yika Irin Alagbara Irin:

Iwọn opin	Apẹrẹ iwuwo	Dia	Apẹrẹ iwuwo
(mm)	fun mita kan (kg)	(ninu)	fun mita kan (kg)
3mm	0.06	1/8 ″	0.06
4mm	0.10	3/16 ″	0.14
5mm	0.16	1/4 ″	0.25
6mm	0.22	5/16 ″	0.39
7mm	0.30	3/8 ″	0.56
8mm	0.40	7/16 ″	0.77
10mm	0.62	1/2 ″	1.00
12mm	0.89	9/16 ″	1.22
14mm	1.22	5/8 ″	1.56
15mm	1.40	11/16 ″	1.89
16mm	1.59	3/4 ″	2.25
18mm	2.01	7/8 ″	3.07
20mm	2.48	1 ″	4.03
22mm	3.00
24mm	3.57
25mm	3.88